ETUDE DU RENFORCEMENT D'ADHERENCE DE COUCHES D'ALUMINIU DEPOSEES PAR PULVERISATION RF SUR DU POLYMETHACRYLATE DE METHYLE. EFFET D'UN PRETRAITEMENT DE SURFACE PLASMA / KAMAL AMGAAD ; SOUS LA DIRECTION DE MICHEL CAILLER

Date :

Editeur / Publisher : [S.l.] : [s.n.] , 1993

Format : 169 P.

Type : Livre / Book

Type : Thèse / Thesis

Langue / Language : français / French

Adhésion (physique)

Université de Nantes (1962-2021) (Organisme de soutenance / degree-grantor)

Relation : ETUDE DU RENFORCEMENT D'ADHERENCE DE COUCHES D'ALUMINIU DEPOSEES PAR PULVERISATION RF SUR DU POLYMETHACRYLATE DE METHYLE. EFFET D'UN PRETRAITEMENT DE SURFACE PLASMA / Kamal Amgaad ; sous la direction de Michel Cailler / Grenoble : Atelier national de reproduction des thèses , 1993

Résumé / Abstract : CETTE ETUDE PORTE SUR LE RENFORCEMENT D'ADHERENCE DE COUCHES MINCES D'ALUMINIUM, DEPOSEES PAR PULVERISATION RF, SUR DES SUBSTRATS EN POLYMETHACRYLATE DE METHYLE AYANT SUBI UN PRETRAITEMENT DE SURFACE, PAR PLASMA, DANS TROIS ATMOSPHERES DIFFERENTES (ARGON, ARGON+OXYGENE, AZOTE). LA CARACTERISATION MECANIQUE DE LA FORCE DE LIAISON DEPOT-SUBSTRAT A ETE FAITE A L'AIDE DU TEST DE LA RAYURE. LES RESULTATS OBTENUS ONT MONTRE QU'AUCUN ACCROISSEMENT DE LA CHARGE CRITIQUE NE SE PRODUISAIT AVEC L'ARGON. DANS LES DEUX AUTRES CAS (PLASMAS REACTIFS), UN ACCROISSEMENT NOTABLE DE CETTE MEME CHARGE CRITIQUE POUVAIT ETRE OBSERVE, POUR UNE DUREE ADEQUATE DU TRAITEMENT, UN TRAITEMENT EXCESSIF ENTRAINANT UNE PERTE D'ADHERENCE. PAR AILLEURS, LES MESURES D'ANGLE DE CONTACT ONT MONTRE QU'UNE EGALE BONNE MOUILLABILITE ETAIT OBTENUE, DES LES PREMIERES MINUTES DE TRAITEMENT, QUELLE QUE SOIT LA NATURE DU GAZ PLASMAGENE UTILISE. LES CHANGEMENTS, CREES A LA SURFACE DU SUBSTRAT, AU COURS DES DIFFERENTS TRAITEMENTS ONT ETE ETUDIES PAR MICROSCOPIE A BALAYAGE ET PAR SPECTROSCOPIE INFRAROUGE (FTIR-ATR) ET DE PHOTOELECTRONS X (XPS). DES EXAMENS DU DOMAINE INTERFACIAL ONT EGALEMENT ETE FAITS PAR XPS ET PAR MICROSCOPIE ELECTRONIQUE A TRANSMISSION (MET). LES RESULTATS OBTENUS ONT MONTRE QUE LE RENFORCEMENT D'ADHERENCE S'ACCOMPAGNAIT D'UN CHANGEMENT DE MORPHOLOGIE DES SURFACES TRAITEES, POUVANT FACILITER L'ANCRAGE DU DEPOT METALLIQUE SUR SON SUBSTRAT. LES OBSERVATIONS AU MET SUGGERENT FORTEMENT QU'UN TEL MECANISME INTERVIENT. CEPENDANT, LE MECANISME MIS EN JEU EST VRAISEMBLABLEMENT PLUS COMPLEXE CAR DE NOUVELLES LIAISONS SONT EGALEMENT OBSERVEES DANS LE DOMAINE INTERFACIAL. DE MEME, ON PEUT CONSIDERER QUE L'ACCROISSEMENT DE LA CHARGE CRITIQUE PEUT PROVENIR DE L'ELIMINATION DES COUCHES SUPERFICIELLES, DE FAIBLE COHESION, PRESENTES INITIALEMENT A LA SURFACE DU POLYMERE