Résumé / Abstract : LES MECANISMES DE FORMATION DE MEMBRANES DESTINEES A L'ENCAPSULATION D'ILOTS DE LANGERHANS, PAR PRECIPITATION VIA IMMERSION DANS L'EAU DES SOLUTIONS DE POLYAMIDE 4,6 (PA4,6) DANS L'ACIDE FORMIQUE ET DES SOLUTIONS DE COPOLYMERES ACRYLONITRILE DANS LE DIMETHYLSULFOXYDE ONT ETE ETUDIES. POUR PALLIER L'IMPOSSIBILITE D'OBTENIR LE PA4,6 AMORPHE A TEMPERATURE AMBIANTE, NOUS AVONS DEFINI UNE NOUVELLE METHODE DE CALCUL DU TAUX DE CRISTALLINITE BASEE SUR L'ANALYSE PAR RAYONS X AUX GRANDS ANGLES DU POLYMERE BRUT A L'ETAT FONDU. CECI A PERMI D'ETUDIER LA VARIATION DES TAUX DE CRISTALLINITE ET L'EVOLUTION MORPHOLOGIQUE DES MEMBRANES EN FONCTION DE LA CONCENTRATION EN PA4,6, DE L'ADDITION D'EAU A LA SOLUTION INITIALE, DE L'INTRODUCTION D'UNE PHASE D'EVAPORATION PREALABLE DU SOLVANT, DU CHOIX DU SUPPORT SUR LEQUEL EST DEPOSEE LA SOLUTION ET DE LA MASSE MOLECULAIRE DU PA4,6. AINSI, LES MEMBRANES, A PRIORI LES PLUS INTERESSANTES, PROVIENNENT D'UN PROCESSUS DE PRECIPITATION AVEC EVAPORATION PREALABLE DU SOLVANT. AFIN D'AUGMENTER LA POROSITE DE CES MEMBRANES, L'INFLUENCE DE L'ADDITION DE POLYVINYLPYRROLIDONE OU DE POLYOXYDE D'ETHYLENE A ETE ETUDIEE SUR LES MECANISMES DE PRECIPITATION, LES STRUCTURES ET LES TAUX DE CRISTALLINITE DES MEMBRANES. PARALLELEMENT, DES COPOLYMERES D'ACRYLONITRILE, D'ACRYLATE DE METHYLE ET DE METHACRYLATE DE MONOPOLYETHYLENEGLYCOL ONT ETE SYNTHETISES PAR POLYMERISATION RADICALAIRE DANS LE DIMETHYLSULFOXYDE. EN FIN DE POLYMERISATION, TROIS SOLUTIONS DIFFERANT SELON LA COMPOSITION DU COPOLYMERE, LEUR CONCENTRATION EN COPOLYMERE ET LEUR VISCOSITE ONT ETE UTILISEES POUR PREPARER DES MEMBRANES. CES DERNIERES REPONDENT MIEUX AUX CRITERES NECESSAIRES A L'ENCAPSULATION D'ILOTS DE LANGERHANS QUE LES MEMBRANES EN PA4,6. EN EFFET, LEUR STRUCTURE ASYMETRIQUE ASSURE LES PROPRIETES DE PERMEABILITE SELECTIVE ALORS QU'EN FAISANT VARIER LA COMPOSITION DU COPOLYMERE, LES TAUX D'ADSORPTION PROTEIQUES DES MEMBRANES PEUVENT ETRE NOTABLEMENT REDUITS